… CEWELD 8812-Co-45 the dense and smooth layers with hardness of up to 1200 HV0.1 and tensile strength acc. to DIN 50160 of more than 70 MPa are frequently used without further treatment. … μm FSSS Apparent density (ISO 3923-2): 4.2-5.5 g/cm³ Particle shape: preponderantly spherical Particle size: 45/20 μm … Ideal for use in a …

… Excellent weldabillity and improved mechanical strength due to its high Nickel content. The weld deposit is … and cleaning method during production.  Thicker sections should be preheated (150°C) prior to welding. … Filler metal for welding …

… Austenitic deposit with strain hardening properties and no limits in the number of layers. The deposit is non magnetic and can not be flame cut. Extreme resistance to heavy impact loads. … properties. This alloy should be applied at highest impact and pressure loads applications. Best to be used with welding flux FL 915 … …

… Smooth drop transfer and more stable arc compare to solid wires. High productivity and weldabillity, better … hand welding. Excellent against pitting and stress corrosion. The PREN above 35 weldmetal offers outstanding resistance against pitting. … ISO 15608: (8.1), 10.1-10.2,  TÜV 1000: Gr. 31, DUPLEX 2209, 22%Cr 9%Ni 3%Mo  …

… CEWELD® SA 318 is engineered to a very precise analysis to create a … CrNiMo 17 12 2, G-X 6 CrNiMo 18 10,         X 5 CrNiMo 17 13 3 UNS S31600, S31603, S31635, S31640, S31653,  AISI 316, 316L, 316Ti, 316Cb    … …

… Afin de vous garantir que les conseils que vous recherchez seront donnés par des professionnels et des experts dans leur … de soudage. Dans le cadre de cette politique, le CEWELD® Select Dealer prend une position particulière. Ces spécialistes du soudage ont choisi …

… The weld deposit offers good wear and corrosion resistance even in seawater. Welding instructions: - Preheating for sections >6 mm from 150 till 300 ºC is recommended. Use … Aluminium Bronze or Copper, etc. Mat.n: 2.0916, 2.0920, 2.0928, 2.0460, 2.0932  CuAl5, CuAl8, G-CuAl9,  CuZn20Al2, CuAl8Fe3,   UNS: C60600, …

… This pure aluminum filler metal offers excellent weldability when properly cleaned prior to welding. Heavy parts and thicker plates should be preheated (150°C), prior to welding  … Cast aluminium special repairs, …

… Grâce au processus de fabrication et au double recuit à 580ºC pendant le processus d'étirage, la teneur en hydrogène de …

… 4130 offers extreme high strength with excellent ductility and good weldabillity. Preheat and interpass temperature > 200°C …  1.7218, 1.7225 25 CD4, 13 …